Michem® Flex P1850

Brand Family Overview

Mold Release is a solventborne polyethylene emulsion that eliminates the high stress between a mold and the molded part, typically used for ceramics. It allows for movement and shrinkage of the part during processing and subsequent temperature fluctuations. With Mold Release, the part releases clean.

See more Mold Release products.


Promotes adhesion to extrusion coated resins resulting in exceptionally high bond strength for film, metal and paper substrates. This product is recommended for off-line processes as it will not block in a rewound roll.


Water based primer for liquids and extrusion coated resins.

Performance Attributes

This product is used in many applications including the following:

ApplicationProperties Imparted
Extrusion Coating Primersadhesion for film

See more products recommended for Extrusion Coating Primers.
Physical Properties

These physical properties are typical but should not be considered specifications.

AppearanceWhite, translucent liquid
Percent Non-Volatile30.0 - 32.0
Brookfield Viscosity (cps, mPa·s) <100
Spindle Number1

Site of Manufacture (and Product Code)

CIN (MFP1850)
AUB (MFP1850.E)
SNG (MFP1850.S)

Application Data

Michem®Flex P1850 may be applied via flexo, gravure or smooth roll coater. Corona or flame treat substrates prior to priming and dry thoroughly with hot, circulating air. This product is best for off-line processes, as it will not block in a rewound roll. Recommended application weight for film substrates is between 0.1 - 1.0 dry g/m2.


Ensure adequate ventilation. Handle in accordance with good industrial hygiene and safety practice.