Michem® Flex P1883

Brand Family Overview

Mold Release is a solventborne polyethylene emulsion that eliminates the high stress between a mold and the molded part, typically used for ceramics. It allows for movement and shrinkage of the part during processing and subsequent temperature fluctuations. With Mold Release, the part releases clean.

See more Mold Release products.


Primer for metal and paper substrates promoting good adhesion to extrusion coated resins resulting in strong bond strength as well as excellent water and chemical resistance. It may also be used as a low temperature heat seal coating for bonding aluminum foil to itself or to paper.


Water based heat seal coating and primer for extrusion coated resins.

Performance Attributes

This product is used in many applications including the following:

ApplicationProperties Imparted
Heat Seal Coatingsmetal, Substrate - paper
Extrusion Coating Primersadhesion for metal and paper, chemical resistance, water resistance

See more products recommended for Heat Seal Coatings.
See more products recommended for Extrusion Coating Primers.
Physical Properties

These physical properties are typical but should not be considered specifications.

AppearanceTranslucent liquid
Percent Non-Volatile24.2 - 25.4
Brookfield Viscosity (cps, mPa·s) 50 - 400
Spindle Number2

Site of Manufacture (and Product Code)

CIN (MFP1883)
AUB (MFP1883.E)
SNG (MFP1883.S)

Application Data

Michem® Flex P1883 may be applied via flexo, gravure or smooth roll coater. When possible, corona or flame treat substrates prior to priming and dry thoroughly with hot, circulating air. May be used for in-line or off-line processes. Recommended application weight as an extrusion primer is between 0.1 - 1.0 dry g/m2. Heat seal coatings require heavier application weights, typically 1-3 dry g/m2. EZ Cup Viscosity - #3 Cup, 17 - 19 sec.


Ensure adequate ventilation. Handle in accordance with good industrial hygiene and safety practice. Use personal protective equipment as required.