Michem® Flex P1883
Brand Family Overview
U-Nyte™ products are fiberglass mat binders formulated with phenoxy toughened epoxy resin and compounded with a curing agent. They are used in the manufacturing of nonwoven and textile rolled goods, are compatible with vinyl ester, unsaturated polyester, epoxy and urethane, and are available in powder and flake form.See more U-Nyte products.
Primer for metal and paper substrates promoting good adhesion to extrusion coated resins resulting in strong bond strength as well as excellent water and chemical resistance. It may also be used as a low temperature heat seal coating for bonding aluminum foil to itself or to paper.
Water based heat seal coating and primer for extrusion coated resins.
This product is used in many applications including the following:
|Heat Seal Coatings||metal, Substrate - paper|
|Extrusion Coating Primers||adhesion for metal and paper, chemical resistance, water resistance|
See more products recommended for Heat Seal Coatings.
See more products recommended for Extrusion Coating Primers.
These physical properties are typical but should not be considered specifications.
|pH||8.4 - 9.4|
|Emulsifier Charge||Ammoniated dispersion|
|Percent Non-Volatile||24.2 - 25.4|
|Recommended pH Range||>7|
|Brookfield Viscosity (cps, mPa·s)||50 - 400|
Site of Manufacture (and Product Code)
Michem® Flex P1883 may be applied via flexo, gravure or smooth roll coater. When possible, corona or flame treat substrates prior to priming and dry thoroughly with hot, circulating air. May be used for in-line or off-line processes. Recommended application weight as an extrusion primer is between 0.1 - 1.0 dry g/m2. Heat seal coatings require heavier application weights, typically 1-3 dry g/m2. EZ Cup Viscosity - #3 Cup, 17 - 19 sec.
Ensure adequate ventilation. Handle in accordance with good industrial hygiene and safety practice. Use personal protective equipment as required.