Michem® Flex P1309
Brand Family Overview
Michem® Coat water-based coatings are selected primarily for grease and oil resistance. Other benefits include water resistance, release, coldset gluability, hot melt gluability, recyclability, and compliance with specific food contact regulations.See more Michem Coat products.
A primer for film, metalized film, printed film and paper substrates promoting excellent adhesion to extrusion coated resins, resulting in high bond strength for dry and low moisture content products. Michem Flex P1309 creates very strong adhesion between treated film and PE and EVA extrudates.
Water-based primer for polyethylene extrusion and anchor coating
This product is used in many applications including the following:
|Extrusion Coating Primers||adhesion for film, adhesion for metal and paper|
See more products recommended for Extrusion Coating Primers.
These physical properties are typical but should not be considered specifications.
|pH||10.0 - 12.0|
|Shelf Life (mo)||12|
|Freeze/Thaw Stability||Stable after 5 Cycles|
|Percent Non-Volatile||4.5 - 5.5|
|Specific Gravity||1.01 - 1.04|
|Brookfield Viscosity (cps, mPa·s)||0 - 50|
Site of Manufacture (and Product Code)
Michem® Flex P1309 may applied via flexo, gravure or smooth roll coater. It can be diluted 1:1 with water or with a 50:50 pre-mixture of water and isopropyl alcohol prior to use. It has good compatibility with both Ethanol & Methanol but limited compatibility in IPA solvent. It is recommended that IPA must always be diluted with water before use. It is recommended to corona or flame-treat substrates prior to priming and dry thoroughly with hot, circulating air. This product is highly recommended for application in-line to a target coat weight on film substrates of 0.025 0.075 dry g/m2.