Michem® Flex P2300
Primer for film, metalized film, printed film, and paper substrates promoting excellent adhesion to extrusion coated resins resulting in high bond strength for dry and low moisture contents. It creates very strong adhesion between treated film and PE extrudate. It may also be used on film substrates to promote adhesion to liquid top coats such as Michelman heat seal coatings and acrylic coatings.
Water based primer for extrusion coating.
This product is used in many applications including the following:
|Extrusion Coating Primers||adhesion for film, adhesion for metal and paper|
See more products recommended for Extrusion Coating Primers.
These physical properties are typical but should not be considered specifications.
|EZ Cup Viscosity (s)||16 - 18|
|pH||9.5 - 11.5|
|Shelf Life (mo)||12|
|Freeze/Thaw Stability||Stable after 5 Cycles|
|Percent Non-Volatile||4.5 - 5.5|
|Specific Gravity||0.99 - 1.01|
|Brookfield Viscosity (cps, mPa·s)||<50|
Site of Manufacture (and Product Code)
Michem® Flex P2300 may be applied via flexo, gravure or smooth roll coater. Dilute 1:1 with water prior to use. Corona or flame treat substrates prior to priming and dry thoroughly with hot, circulating air. This product is best for in-line processes. Recommended application weight for film substrates is 0.025 - 0.075 dry g/m2 (0.5-1.5 wet g/m2). EZ Cup Viscosity - #2 Cup, 16-18 sec.